63 Works

Test data for low cycle fatigue - strain control on material U 720 at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 carb at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material 10 CrMo 9 10 at 500 Celsius

S Nishijima &
This data collection was created during a VAMAS round robin uniaxial creep study on material 10 CrMo9 10 at temperatures between 450 and 600 Celsius.

Test data for uniaxial creep on material 10 CrMo 9 10 at 475 Celsius

S Nishijima &
This data collection was created during a VAMAS round robin uniaxial creep study on material 10 CrMo9 10 at temperatures between 450 and 600 Celsius.

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 carb at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 carb at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material U 720 carb at 750 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material CM 247 ds lc carb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material IN792 ds decarb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 ta at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 mod - sj at 550 Celsius

P Haehner & Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M Project, JRC-IET was engaged with uniaxial creep tests parent material, X-welds and weld material of P91. In addition to the test programme metallographic investigations on damage development were perfomed. Specimens for mechanical testing were selected from a welded joint. The weldment was produced by narrow gap TIG welding on modified 9% Chromium steel (P91). The plate is 150 mm thick and the weldment has...

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 mod at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material P91 wm at 550 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for low cycle fatigue - strain control on material U 720 carb at 650 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material U 720 carb at 750 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material CM 247 ds lc carb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material CM 247 ds lc carb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material CM 247 ds lc decarb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...

Test data for uniaxial creep on material CM 247 ds lc decarb at 850 Celsius

& Institute For Energy EC-JRC Petten
As a part of the overall test programme of FP5 HTR-M1 Project, JRC-IET performed a series of uni-axial creep and low-cycle fatigue (LCF) tests on the nickel based superalloy Udimet 720 material with the objective of assessing the effect of a specific HTR operating environment. Tests were performed on as-received, heavily carburized, decarburized, and thermally aged material. The heavily carburized state was achieved by exposure for 1000h at 950 Celsius in a 1.6 bar absolute...