3,058 Works

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 13.52 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 49.99 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 39.85 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 65.03 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 29.48 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 26 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 24.38 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 54.44 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 54.03 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 34.04 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 34.48 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 69.64 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 78.88 MPa (repeat test)

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 90.75 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 91.09 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 26.01 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 48.56 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 48 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 40 MPa (second repeat test)

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial tensile on material INCONEL 617 irr at 20 Celsius

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 61.12 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 35 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 90 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 44 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 20 MPa (third repeat test)

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...