Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 64.93 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 65.23 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 65.02 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 20 MPa (second repeat test)

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 50.01 MPa (repeat test)

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 50.05 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 17 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for low cycle fatigue - strain control on material P91 ar - sj at 550 Celsius (thirteenth repeat test)

&
Fatigue tests on 9Cr welded joints and weld metal

Test data for low cycle fatigue - strain control on material P91 ar - sj at 550 Celsius (eighth repeat test)

&
Fatigue tests on 9Cr welded joints and weld metal

Test data for uniaxial tensile on material P91 nt at 500 Celsius (repeat test)

&
The present test data sets have been generated by KAERI in the scope of the MATTER project.

Test data for uniaxial tensile on material P91 nt at 500 Celsius

&
The present test data sets have been generated by KAERI in the scope of the MATTER project.

Test data for uniaxial tensile on material P91 nt at 550 Celsius (repeat test)

&
The present test data sets have been generated by KAERI in the scope of the MATTER project.

Test data for uniaxial creep on material P91 nt at 600 Celsius and a stress of 150 MPa

&
The present test data sets have been generated by KAERI in the scope of the MATTER project.

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 58.46 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 44.04 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 800 Celsius and a stress of 76.85 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 44 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 900 Celsius and a stress of 36.76 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 20.62 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 27.81 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 50.07 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 26.08 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 850 Celsius and a stress of 64.22 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 27.08 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...

Test data for uniaxial creep on material INCONEL 617 at 950 Celsius and a stress of 27 MPa

&
The Alloy 617 creep rupture data were determined for the high temperature reactor projects (the direct cycle helium turbine project, the nuclear process heat project and the district heating project) of the Federal Republic of Germany and the State of North Rhine Westphalia, the aim being to qualify the alloy for service at temperatures up to 950°C. Alloy 617 was the prime candidate alloy for construction of the He-He intermediate heat exchanger and hot gas...