Small punch creep test data for 2.25 Cr 1Mo V mod material at 580 °C and a load of 340 N (third repeat test)

& Institute For Energy EC-JRC Petten
Data collection created in the scope of a programme designed to evaluate the reliability of the Small Punch (SP) testing method as an alternative mechanical test technique for evaluation of the residual life and integrity assessment of components in ageing plants. Tests were performed on the low alloy - 2¼Cr 1Mo V modified ferritic steel, widely selected for construction of high temperature components in petrochemical plants. The technique was shown to facilitate determination of both...

Small punch creep test data for 2.25 Cr 1Mo V mod material at 560 °C and a load of 340 N (ninth repeat test)

& Institute For Energy EC-JRC Petten
Data collection created in the scope of a programme designed to evaluate the reliability of the Small Punch (SP) testing method as an alternative mechanical test technique for evaluation of the residual life and integrity assessment of components in ageing plants. Tests were performed on the low alloy - 2¼Cr 1Mo V modified ferritic steel, widely selected for construction of high temperature components in petrochemical plants. The technique was shown to facilitate determination of both...

Small punch tensile/fracture test data for 2.25 Cr 1Mo V mod material at 25 °C and a displacement rate of .003 mm/s (twenty-second repeat test)

& Institute For Energy EC-JRC Petten
Data collection created in the scope of a programme designed to evaluate the reliability of the Small Punch (SP) testing method as an alternative mechanical test technique for evaluation of the residual life and integrity assessment of components in ageing plants. Tests were performed on the low alloy - 2¼Cr 1Mo V modified ferritic steel, widely selected for construction of high temperature components in petrochemical plants. The technique was shown to facilitate determination of both...

Small punch tensile/fracture test data for 2.25 Cr 1Mo V mod material at 25 °C and a displacement rate of .003 mm/s (nineteenth repeat test)

& Institute For Energy EC-JRC Petten
Data collection created in the scope of a programme designed to evaluate the reliability of the Small Punch (SP) testing method as an alternative mechanical test technique for evaluation of the residual life and integrity assessment of components in ageing plants. Tests were performed on the low alloy - 2¼Cr 1Mo V modified ferritic steel, widely selected for construction of high temperature components in petrochemical plants. The technique was shown to facilitate determination of both...

Small punch tensile/fracture test data for P92 nt material at 20.5 °C and a displacement rate of .00833 mm/s

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Small punch tensile/fracture test data for P92 material at 23 °C and a displacement rate of .00833 mm/s

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Small punch tensile/fracture test data for P92 material at 22 °C and a displacement rate of .00833 mm/s

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Small punch tensile/fracture test data for P92 material at 23 °C and a displacement rate of .00833 mm/s (fourth repeat test)

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Small punch tensile/fracture test data for P92 nt material at -164 °C and a displacement rate of .00833 mm/s

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Small punch tensile/fracture test data for P92 nt material at -129 °C and a displacement rate of .00833 mm/s

&
Small punch tensile and creep data obtained in a round robin exercise for the elaboration of an EN standard on small punch testing. For estimating the tensile properties a series of tests were carried out at room temperature on Gr. 91 steel with different heat treatments. Further tests were performed at varying temperatures between 77K and room temperature to determine the ductile to brittle transition temperature (DBTT). Creep tests were carried out at temperatures in...

Uniaxial tensile test data for 14 MoV 6 3 se material at 600 °C

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 550 °C and a stress of 160 MPa

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 se material at 625 °C and a stress of 55 MPa (third repeat test)

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial tensile test data for 13 CrMo 4 4 material at 20 °C

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial tensile test data for 13 CrMo 4 4 material at 530 °C

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial tensile test data for 13 CrMo 4 4 material at 600 °C

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial tensile test data for 14 MoV 6 3 material at 560 °C

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 550 °C and a stress of 165 MPa

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 600 °C and a stress of 130 MPa

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 530 °C and a stress of 140 MPa (third repeat test)

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 550 °C and a stress of 200 MPa (second repeat test)

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 material at 530 °C and a stress of 140,2 MPa

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 14 MoV 6 3 material at 625 °C and a stress of 160 MPa

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 14 MoV 6 3 material at 550 °C and a stress of 165 MPa (third repeat test)

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...

Uniaxial creep test data for 13 CrMo 4 4 se material at 530 °C and a stress of 130 MPa (third repeat test)

&
This data collection consists of uniaxial creep, uniaxial tensile, and elastic modulus results from tests performed on low-alloy steels at FZ Jülich in the scope of COST 501/II/WP5 C. With COST 501 Round II Work Package 5 concerned with the prediction of residual lifetime under simulated service loads, the WP5 C sub-package was focused on steam pipe steels.In the scope of the WP5 C sub-package, creep rupture testing of 13CrMo 4 4 (1Cr0.5Mo0.25V) and 14MoV...