James H. Havens & Robert C. Deen
Repeated stressing of metals above certain limits induces inter- and intra-crystalline dislocations and cleavages and eventually cracks which propagate to failure. Some authorities consider crack propagation to be a separate and discrete stage in the failure process. The internal damage is insidiously cumulative and irreversible. This phenomenon was recognized as early as 1829 and was termed fatigue as early as 1839(1). From the beginning of fatigue testing (Wohler, 1858-1870), results have been reported as S-N,...