MICROSTRUCTURE CHARACTERIZATION OF WELD CONSUAMBLE CONDITION ON RESIDUAL STRESS, FLEXURAL STRENGTH AND ROOM TEMPERATURE TENSILE TESTS of P92 STEEL

V.K. Pal & L.P. Singh
The present manuscript describes the flexural strength, lower critical stress, and tensile stress of P92 steel welds was determined with respect to different conditions. The residual stresses axial and transverse stress were also measured blind hole drilling methods for the different conditions of welding consumables. The peak value of residual stresses was measured at the centre of the fusion zone. The maximum value of transverse stress was measured to be 355 MPa for case IV...