Aging Effect on Microstructure and Machinability of Corrax Steel

A. S. Guldibi & H. Demir
In this paper, the influence of the aging process on the microstructure and machinability of Corrax Steel was investigated for four samples: a solution heat-treated (A0) and three samples aged at 400ºC (A4), 525ºC (A5.25) and 600ºC (A6) for four hours. The effect of aging temperature on hardness was examined. Machining tests were carried out using a CNC lathe with a multi-layer coated PVD (AlTiN) cutting tool, at various cutting speeds (50, 100, 150, 200,...