The Immersion Corrosion Resistance of Shot Peening and MAO Applied on AZ31−0.5% La Sheets

G. Elmansouri, I. H. Kara, H. Ahlatci & Y. Turen
In this study, the effect of Shot Peening (SP) and Micro Arc Oxidation (MAO) process on the corrosion resistance of 0.5% La with added AZ31 Mg alloy, hot rolled at different rolling speeds, was investigated. It was found that the surface of the rolled material at a rolling speed of 4.7m/min had higher surface smoothness values than the one rolled at 10m/min. It was observed that the corrosion rate changed in the first 40 of...